Fabrication of flexible thermoelectric microcoolers using planar thin-film tech...

• Autor(es): Gonçalves, L. M. ; Rocha, J. G. ; Couto, Carlos ; Alpuim, P. ; Min, Gao ; Rowe, D. M. ; Correia, J. H.
• Data: 2007
• Identificador Persistente: http://hdl.handle.net/1822/8640
• Origem: RepositóriUM - Universidade do Minho
• Assunto(s): Peltier; Flexible
• Tipo de Documento: Artigo
• Idioma: Inglês

Descrição

The present work reports on the fabrication and characterization of a planar Peltier cooler on a flexible substrate. The device was fabricated on a 12 νm thick Kapton(c) polyimide substrate using Bi2Te3 and Sb2Te3 thermoelectric elements deposited by thermal co-evaporation. The cold area of the device is cooled with four thermoelectric junctions, connected in series using metal contacts. Plastic substrates add uncommon mechanical properties to the composite film-substrate and enable integration with novel types of flexible electronic devices. Films were deposited by co-evaporation of tellurium and bismuth or antimony to obtain Bi2Te3 or Sb2Te3, respectively. Patterning of the thermoelectric materials using lift-off and wet-etching techniques was studied and compared. The performance of the Peltier microcooler was analysed by infrared image microscopy, on still-air and under vacuum conditions, and a maximum temperature difference of 5 °C was measured between the cold and the hot sides of the device. © 2007 IOP Publishing Ltd.