Fluorescence in nanostructured fulleride films
Descrição
Applied Physics Letters, 89 Nanostructuring of fullerene C60 beam deposited films is achieved by electrochemical reduction in a potassium hydroxide aqueous solution. Alkali fulleride clusters are formed at the electrode, as it is illustrated by cyclic voltammetry, x-ray diffraction, and scanning tunneling microscopy. Fluorescence emission from fluorophore doped fullerene reduced films was investigated by fluorescence spectroscopy and scanning near-field optical microscopy. These techniques lead to results which also fit such nanometer-sized fulleride cluster interpretation. In particular, the fluorophore fluorescence lifetime decreases as long as aggregation in the film is more effective,which occurs with the increase of film thickness.
Applied Physics Letters, 89 Nanostructuring of fullerene C60 beam deposited films is achieved by electrochemical reduction in a potassium hydroxide aqueous solution. Alkali fulleride clusters are formed at the electrode, as it is illustrated by cyclic voltammetry, x-ray diffraction, and scanning tunneling microscopy. Fluorescence emission from fluorophore doped fullerene reduced films was investigated by fluorescence spectroscopy and scanning near-field optical microscopy. These techniques lead to results which also fit such nanometer-sized fulleride cluster interpretation. In particular, the fluorophore fluorescence lifetime decreases as long as aggregation in the film is more effective,which occurs with the increase of film thickness.
Tipo de Documento
Artigo
Idioma Inglês
Idioma Inglês
| Financiadores do RCAAP | |||||||
|
|
|
|
|
|
||