Padrão, Jorge 
; Silva, João P. ; Rodrigues, Ligia R. ; Dourado, Fernando ; Lanceros-Mendez, Senentxu ; Sencadas, Vitor
Data: 2014
Identificador Persistente: http://hdl.handle.net/11110/632
Origem: CiencIPCA
Assunto(s): Gelatin; Electrospun; Polypeptides; Cross-linking; Water Vapor permeability; Cytocompatibility; Barrier Properties
Descrição
Development of suitable membranes is a fundamental requisite for tissue and biomedical engineering applications. This work presents fish gelatin random and aligned electrospun membranes cross-linked with glutaraldehyde (GA). It was observed that the fiber average diameter and the morphology is not influenced by the GA exposure time and presents fibers with an average diameter around 250 nm. Moreover, when the gelatin mats are immersed in a phosphate buffered saline solution (PBS), they can retain as much as 12 times its initial weight of solution almost instantaneously, but the material microstructure of the fiber mats changes from the characteristic fibrous to an almost spherical porous structure. Cross-linked gelatin electrospun fiber mats and films showed a water vapor permeability of 1.37 ± 0.02 and 0.13 ± 0.10 (g.mm)/(m2.h.kPa), respectively. Finally, the processing technique and cross-linking process does not inhibit MC-3T3-E1 cell adhesion. Preliminary cell culture results showed good cell adhesion and proliferation in the cross-linked random and aligned gelatin fiber mats. This work is funded by FEDER funds through the "Programa Operacional Factores de Competitividade – COMPETE" and by national funds arranged by FCT- Fundação para a Ciência e a Tecnologia, project references NANO/NMed-SD/0156/2007, PTDC/CTM-NAN/112574/2009 and PEST-C/FIS/UI607/2011. The authors also thank funding from Matepro –Optimizing Materials and Processes”, ref. NORTE-07-0124-FEDER-000037”, co-funded by the “Programa Operacional Regional do Norte” (ON.2 – O Novo Norte), under the “Quadro de Referência Estratégico Nacional” (QREN), through the “Fundo Europeu de Desenvolvimento Regional” (FEDER). The authors also thank support from the COST Action MP1003, 2010 ‘European Scientific Network for Artificial Muscles’. VS, JP and JS thank the FCT for the SFRH/BPD/64958/2009, SFRH/BD/64901/2009, and SFRH/BPD/63148/2009 grants, respectively.