Assunto(s): High speed drilling; Carbon fibre reinforced plastics; Composite laminate; Delamination; Response surface methodology
Descrição
Dissertação para obtenção do Grau de Doutor em
Engenharia Mecânica The tremendous growth which occurs at a global level of demand and use of composite materials brings with the need to develop new manufacturing tools and methodologies. One of the major uses of such materials, in particular plastics reinforced with carbon fibres, is their application in structural components for the aircraft industry with low weight and high stiffness. These components are produced in near-final form but the so-called secondary processes such as machining are often unavoidable. In this type of industry, drilling is the most frequent operation due to the need to obtain holes for riveting and fastening bolt assembly of structures. However, the problems arising from drilling, particularly the damage caused during the operation, may lead to rejection of components because it is an origin of lack of resistance. The delamination is the most important damage, as it causes a decrease of the mechanical properties of the components of an assembly and, irrefutably, a reduction of its reliability in use. It can also raise problems with regard to the tolerances of the assemblies. Moreover, the high speed machining is increasingly recognized to be a manufacturing technology that promotes productivity by reducing production times. However, the investigation whose focus is in high speed drilling is quite limited, and few studies on this subject have been found in the literature review. Thus, this thesis aims to investigate the effects of process variables in high speed drilling on the damage produced. The empirical models that relate the delamination damage, the thrust force and the torque with the process parameters were established using Response Surface Methodology. The process parameters considered as input factors were the spindle speed, the feed per tooth, the tool diameter and the workpiece thickness. A new method for fixing the workpiece was developed and tested. The results proved to be very promising since in the same cutting conditions and with this new methodology, it was observed a significant reduction of the delamination damage. Finally, it has been found that is possible to use high speed drilling, using conventional twist drills, to produce holes with good quality, minimizing the damage.