Silica-scavenging effects in ceria-based electrolytes

• Author(s): Ivanova, Daria
• Date: 2009
• Persistent ID: http://hdl.handle.net/10773/2295
• Origin: RIA - Repositório Institucional da Universidade de Aveiro
• Subject(s): Engenharia de materiais; Pós cerâmicos; Electrólitos; Condutividade eléctrica; Sinterização
• Document Type: Master Thesis
• Language: English
• Advisor(s): Marques, Fernando Manuel Bico

Description

Gadolinium-doped ceria based powders were co-fired with additions of silica, and silica and lanthanum oxide, to test the silicascavenging role of lanthanum. The formation of one ionic conducting secondary phase, instead of an insulating phase, was attempted. The structural, microstructural and electrical characterization of these samples confirmed the formation of one apatite-type lanthanum silicate-based phase and a significant enhancement of the grain boundary conductivity of these materials. ABSTRACT: Pós de céria dopada com gadolínio foram sinterizados com adições de sílica, e de sílica e óxido de lantânio, para testar o efeito de remoção de sílica do óxido de lantânio. Com esta abordagem explorou-se a formação de uma fase secundária condutora iónica em vez de uma fase isoladora. A caracterização estrutural, microestrutural e eléctrica das amostras confirmou a formação de uma fase tipo apatite derivada do silicato de lantânio e uma melhoria significativa da condutividade da fronteira de grão destes materiais. Mestrado em Ciência e Engenharia de Materiais