Shrinkage and mechanical performance of geopolymeric mortars based on calcined ...

• Autor(es): Tahri, W. ; Samet, B. ; Torgal, Fernando Pacheco ; Aguiar, J. L. Barroso de ; Jesus, Carlos M. G. ; Baklouti, S.
• Data: 2013
• Identificador Persistente: http://hdl.handle.net/1822/28966
• Origem: RepositóriUM - Universidade do Minho
• Assunto(s): Geopolymeric mortars; Tunisian clay; Unrestrained shrinkage; Modulus of elasticity; Workability; Compressive strength
• Tipo de Documento: Artigo
• Idioma: Inglês

Descrição

"Special Issue for International Congress on Materials & Structural Stability, Rabat, Morocco, 27-30 November 2013" Infrastructure rehabilitation represents a multitrillion dollar opportunity for the construction industry. Since the majority of the existent infrastructures are Portland cement concrete based this means that concrete infrastructure rehabilitation is a hot issue to be dealt with. Geopolymers are novel inorganic binders with high potential to replace Portland cement based ones. Geopolymerization is a complex chemical process evolving various aluminosilicate oxides with silicates under highly alkaline conditions, yielding polymeric units, similar to those of an aluminosilicate glass. So far very few studies in the geopolymer field have addressed the rehabilitation of deteriorated concrete structures. This paper discloses some results of an investigation concerning the development geopolymeric repair mortars based on a calcined Tunisian clay. The results show that Tunisian calcined clay based mortars have hydration products with typical geopolymeric phases. Results also show that the geopolymeric mortar shows a high unrestrained shrinkage behavior and that its modulus of elasticity is below the threshold required for this repair mortars