Poly(vinylidene fluoride-trifluoroethylene) (72/28) interconnected porous membr...

• Author(s): Ferreira, Armando José Barros ; Silva, Jaime ; Sencadas, V. ; Gómez Ribelles, J. L. ; Lanceros-Méndez, S.
• Date: 2011
• Persistent ID: http://hdl.handle.net/1822/16313
• Origin: RepositóriUM - Universidade do Minho
• Subject(s): Biomaterial; Polymer; Ferroelectric
• Document Type: Conference Object
• Language: English

Description

Electroactive macroporous poly[(vinylidene fluoride)-co-trifluoroethylene] mambranes membranes have been processed by solvent evaporation at room temperature with different polymer/solvent concentrations. The pore architecture consists of on an interconnected spherical pores and this morphology is independent of the membrane thickness. The porosity of the produced membranes increases from 57% for the higher polymer concentration in the polymer/solvent solution (15/85), up to 83% for the lowest polymer amount in the polymer/solvent solution. Far infrared and differential scanning calorimetry measurements reveal that the polymer crystallizes in the ferroelectric phase and the polymer/solvent ratio does n’t not changes the Curie transition and the melting temperature of the polymer.