• Author(s): Guedes, A. ; Pinto, A. M. P. ; Vieira, M. F. ; Viana, Filomena
• Date: 2003
• Persistent ID: http://hdl.handle.net/1822/1563
• Origin: RepositóriUM - Universidade do Minho
• Subject(s): TiAl; Joining; Diffusion Brazing; Interface
• Document Type: Article
• Language: English

Description

The joining of Ti-47Al-2Cr-2Nb (at.%) by diffusion brazing at 1000, 1050 and 1100ºC for 10 min, using a Ti-15Cu-15Ni (wt.%) braze alloy was investigated. The icrostructure and the chemical composition of the interfaces were studied by scanning electron microscopy (SEM) and by energy dispersive X-ray scans (EDS), respectively. The reaction between the gamma-TiAl alloy and the braze alloy led to the formation of layered interfaces, which should be essentially composed of alpha2-Ti3Al and of Ti-Ni-Cu-Al and Ti-Ni-Cu intermetallic compounds. Raising the brazing temperature increases the amount of Al rich intermetallic compounds (Ti-Ni-Cu-Al) and the extension of the interface. The increase of the thickness of the interface is primarily due to the growth of the reaction layer formed near the gamma-TiAl alloy.