Autor(es):
Capelo, Sofia 
; Menino Homem, P. ; Cavalheiro, J. ; Fonseca, I. T. E.
Data: 2012
Identificador Persistente: http://hdl.handle.net/10174/8226
Origem: Repositório Científico da Universidade de Évora
Assunto(s): silver; sterling silver; Chapel; Museum; LSV; tarnishing layers
Descrição
This work demonstrates the potentialities of the linear sweep voltammetry (LSV) for monitoring the composition of the tarnishing layers formed on silver and on the silver-copper alloys exposed to atmospheres contaminated with pollutants, such as H2S and chloride ions, among others.
A collection of silver and sterling silver coupons exposed during periods of 1 and 12 months, at the Holy Altar of the Chapel and at the Treasure Room of the Museum, both of the Porto Cathedral (Portugal), with exposures started in march 2010 and ending in march 2011, have been analysed by LSV.
The LSV spectra of blank polished samples as well as samples covered with thin films of silver sulphide and of silver chloride, formed under controlled conditions, respectively: (i) H2S, 1000 ppm, RH= 53% ± 2, T= 21˚C ± 1, over periods of 24, 48 and 72 h and (ii) 3.5% of NaCl, RH=41%, T= 43˚C, periods of 5 h, have been used as references.
The influence of the atmosphere (Chapel and Museum), exposure time (1 and 12 months) and season, in which the exposures were started, (spring, summer, autumn and winter) have been analysed on the LSVs of the coupons exposed to the various conditions.
For the 1 month exposures started in spring the peaks corresponding to the silver sulphide and silver chloride were, as expected, higher on the samples exposed in the Chapel. For the 12 months exposures both peaks have increased in size with the peak assigned to chloride being much higher in the case of the Chapel and the reverse observed in the case of the Museum. The seasonal influence, even for the 1 month exposures was particularly notable on those started in winter with well visible effects on the sulphide and chloride peaks respectively, in the Museum and Chapel exposures.